Synthesis and Characterization of Nano-sized Nitrogen Doped TiO2 by Mechanochemical Method
-
摘要: 采用机械化学法合成了N掺杂纳米TiO2粉末,对所获得的N掺杂TiO2粉末进行了分析与表征.实验结果表明,采用六次甲基四胺(HMT)为N源,将原料TiO2和HMT混合物经过高能球磨处理后,合成的N掺杂TiO2主要为锐钛矿和板钛矿的混晶相,与原料相比具有小的晶粒度和大的比表面积,对波长大于400nm的可见光具有良好的吸收性能,其吸收边红移至530nm.Abstract: Nitrogen doped TiO2 nano-sized powders were prepared by the mechanochemical reaction method and the property of the powders were analyzed and characterized.The mixed powder of doping sources hexamethylenetetramine(HMT)and raw TiO2 was milled by high energy ball mill.The prepared powders mainly consist of anatase and brookite.Compared with raw material,the N-doped powder has smaller particle size and larger specific surface areas.The N-doped powder shows excellent absorption for visible light λ>400 nm, the absorbed band“red shift”to about 530 nm.
-
Keywords:
- titanium dioxide /
- nitrogen /
- doping /
- mechanochemical synthesize
-
-
[1] FUIJISHIMA A,HONDA K.Photolysis of water at a semiconductor electrode[J].Nature,1972,238:37-38.
[2] FUIJISHIMA A,RAO T N,TRYK D A.Titanium dioxide photocatalysis[J].Journal of Photochemistry and Photobiology C:Photochemistry Reviews,2000,1:1-21.
[3] ANPO M,TAKEUCHI M.The design and development of highly reactive titanium oxide photocatalysts operating under visible light irradiation[J].Journal of Catalysis,2003,216:505-516.
[4] 高廉,郑栅.纳米氧化钛光催化材料及应用[M].北京:化学工业出版社,2002:48. [5] ASAHI R,MORIKAWA T,OHWAKI T,et al.Visible-light photocatalysis in nitrogen-doped titanium oxides[J].Science,2001,293:269-271.
[6] IRIE H,WATANABE Y,HASHIMOTO K.Nitrogen-concentration dependence on photocatalytic activity of TiO2-xNx powders[J].Journal Physics Chemical:B,2003,107:5483-5486.
[7] OHNO T,AKIYOSHI M,UMEBAYASHI T,et al.Preparation of S-doped TiO2 photocatalysts and their photocatalytic activities under visible light[J].Applied Catalysis A:General,2004,265:115-121.
[8] LI Y,HWANG D,LEE N H,et al.Synthesis and characterization of carbon-doped titania as an artificial solar light sensitive photocatalyst[J].Chemical Physics Letters,2005,404:25-29.
[9] UMEBAYASHI T,YAMAKI T,ITO H,et al.Band gap narrowing of titanium dioxide by sulfur doping[J].Applied Physics Letters,2002,81:454-456.
[10] OHNO T,MITSUI T,MATSUMURA M.Photocatalytic activity of S-doped TiO2 photocatalyst under visible light[J].Chemistry Letters,2003,32:364-365.
[11] YAMAKI T,SUMITA T,YAMAMOYO S.Formation of TiO2-xFx compounds in fluorine-implanted TiO2[J].Journal Materials Science Letters,2002,21:33-35.
[12] SATO S,NAKAMURA R,ABE S.Visible-light sensitization of TiO2 photocatalysts by wet-method N doping[J].Applied Catalysis A:General,2005,284:131-137.
[13] 李凤生.超细粉体技术[M].北京:国防工业出版社,2000:340. [14] OZAWA T,IWASAKI M,TADA H,et al.Low-temperature synthesis of anatase-brookite composite nanocrystals:the junction effect on photocatalytic activity[J].Journal of Colloid and Interface Science,2005,281:510-513.
[15] OHNO T,TOKIEDA K,HIGASHIDA S,et al.Synergism between rutile and anatase TiO2 particles in photocatalytic oxidation of naphthalene[J].Applied Catalysis A:General,2003,244:383-391.
[16] RODRIGUEZ J A,JIRSAK T,DVORAK J,et al.Reaction of NO2 with Zn and ZnO:Photoemission,XANES,and density functional studies on the formation of NO3[J].Journal Physics Chemical B,2000,104:319-328.
[17] COLE J L,STOUT J D,BURDA C,et al.Highly efficient formation of visible light tunable TiO2-xNx photocatalysts and their transformation at the nanoecale[J].Journal Physics Chemical B,2004,108:1230-1240.
计量
- 文章访问数: 14
- HTML全文浏览量: 0
- PDF下载量: 8
下载: